Mikä on Inconel 600 tehty of% 3f

Mikä on Inconel 600 tehty % 3f

OMINAISUUDET

Corrosion graphic

KORROOSIO KESTÄVYYS

Alloy 600 has outstanding corrosion resistance imparted by the dual corrosion fighting power of chromium and nickel. Chromium resists corrosion from oxidizing media while nickel defends against attack from many reducing agents. Alloy 600 exhibits good corrosion resistance in reducing acids, mildly oxidizing acids, high purity water, and other media. However, Alloy 600 is not suitable for strong oxidizing acids such as hot nitric acid. It is essentially immune to chloride stress corrosion cracking.

Service Temperature

KOHONNUT LÄMPÖTILA VASTUS

Alloy 600 tarjoaa erinomainen hapettumiskestävyys at lämpötilat jopa 2150 astetta F (1177 aste ). Kuitenkin, se on herkkä sulfidaatio hyökkäys.

Mechanical Properties

INCONEL 600 MEKAANINEN OMINAISUUDET

Alloy 600 voi olla toimitettu sisään alempi lujuus % 2c hehkutettu kunto % 2c tai vahvistettu läpi pilger prosessi. seos 600 ylläpitää erinomainen sitkeys tasainen sisään korkeampi lujuus olosuhteet ja ylläpitää sitkeys kryogeeniset lämpötilat.

heat treatment logo

INCONEL 600 LÄMPÖ HOITO

Vaikka seos 400 ei voi olla vahvistettu lämmöllä käsittely % 2c hehkutus tai stressi lievitys ovat yleisesti käytetään jälkeen kuuma työ tai kylmä työskentely toiminnot. stressiä lievittävä on suoritettu at 1400 aste f 7b % 7 b aste f (760 aste 7b % 7 b 5 % 7 d aste ). Stressiä lievittävä suoritetaan kylmän jälkeen työskentely vähentää jäännös jännitys ja estää vääristymä. Hehkutus on suoritettu at 1700 aste F { % 7 b 7d aste ) palauttaa täyte pehmeys.

Workability

TYÖSTETTÄVYYS

Alloy 600 on hyvä kuuma ja kylmä työstettävyys sisään hehkutettu kunto. kuumatyöskentely pitäisi olla tehty yli 1600 aste F (871 aste ) varmistaa riittävä sitkeys % 2c kun taas kylmä työ pitäisi suorittaa alle 1200 aste F (649 astetta ).

Seos 600 on a nikkeli-kromi-rauta kiinteä liuos vahvistettu seos kanssa a nimellinen kemiallinen koostumus 72% 25 kromi% % 2c ja 8% 25 rauta. Se on yleisesti tunnettu kauppa nimi Inconel 600 ja yhteinen nimi UNS N06600.

What is Inconel 600 made of?

Inconel kemiallinen koostumus

ASTE	ELEMENTTI (% BY MASSA)
ASTE	NI	CR	FE		HUOM	CO	MN	CU	AL	TI	SI	C	S	P	B
600	72.0	14.0–17.0	6.0–10.0				1.0	0.5			0.5	0.15	0.015
617	44.2–56.0	20.0–24.0	3.0	8.0–10.0		10.0–15.0	0.5	0.5	0.8–1.5	0.6	0.5	0.15	0.015	0.015	0.006
625	58.0	20.0–23.0	5.0	8.0–10.0	3.15–4.15	1.0	0.5		0.4	0.4	0.5	0.1	0.015	0.015
690	59.5	30	9.2				0.35	0.01	0.02		0.35	0.019	0.003
718	50.0–55.0	17.0–21.0	vaaka	2.8–3.3	4.75–5.5	1.0	0.35	0.2–0.8	0.65–1.15	0.3	0.35	0.08	0.015	0.015	0.006
X-750	70.0	14.0–17.0	5.0–9.0		0.7–1.2	1.0	1.0	0.5	0.4–1.0	2.25–2.75	0.5	0.08	0.01

Inconel ekvivalentti materiaali

STANDARDI	WERKSTOFF NR.	UNS	GOST	AFNOR	JIS		FI	TAI
Inconel 600	2.4816	N06600	МНЖМц 28-2,5-1,5	NC15FE11M	NCF 600	NA 13	NiCr15Fe	ЭИ868
Inconel 601	2.4851	N06601	XH60BT	NC23FeA	NCF 601	NA 49	NiCr23Fe	ЭИ868
Inconel 617	2.4663	N06617
Inconel 625	2.4856	N06625	ХН75МБТЮ	NC22DNB4M	NCF 625	NA 21	NiCr22Mo9Nb	ЭИ602
Inconel 690	2.4642	N06690
Inconel 718	2.4668	N07718
Inconel 725	-	N07725
Inconel X-750	2.4669	N07750

Inconel mekaaninen ominaisuudet

	TIHEYS	SULAMIS PISTE	TENSILE VAHVUUS	TUOTTO VAHVUUS (0.2%OFFSET)	VENYMÄ
600	8.47 g/cm3	1413 tutkinto (2580 tutkinto F)	Psi – 95,000 , MPa – 655	Psi – 45,000 , MPa – 310	40 %
601	8.1 g/cm3	1411 tutkinto (2571 tutkinto F)	Psi – 80,000 , MPa – 550	Psi – 30,000 , MPa – 205	30 %
617	8.3g/cm³	1363 tutkinto	Greater than or equal to 485 MPa	Suurempi kuin tai yhtä suuri to 275 MPa	25 %
625	8.4 g/cm3	1350 tutkinto (2460 tutkinto F)	Psi – 135,000 , MPa – 930	Psi – 75,000 , MPa – 517	42.5 %
690	8.3g/cm³	1363 tutkinto	Suurempi kuin tai yhtä suuri to 485 MPa	Greater than or equal to 275 MPa	25 %
718	8.2 g/cm3	1350 tutkinto (2460 tutkinto F)	Psi – 135,000 , MPa – 930	Psi – 70,000 , MPa – 482	45 %
725	8.31 g/cm3	1271 tutkinto -1343 tutkinto	1137 MPa	827 MPa	20 %
X-750	8.28 g/cm3	1430 tutkinto	1267 MPa	868 MPa	25 %